Booking of modern domestic tanks. Active tank armor Armor for ground vehicles

Very often you can hear how armor is compared in accordance with the thickness of steel plates 1000, 800mm. Or, for example, that a certain projectile can penetrate some “n”-number of mm of armor. The fact is that now these calculations are not objective. Modern armor cannot be described as equivalent to any thickness of homogeneous steel. There are currently two types of threats: projectile kinetic energy and chemical energy. Under the kinetic threat is meant an armor-piercing projectile or, more simply, a blank with great kinetic energy. In this case, it is impossible to calculate the protective properties of the armor based on the thickness of the steel plate. Thus, projectiles with depleted uranium or tungsten carbide pass through steel like a knife through butter, and the thickness of any modern armor, if it were homogeneous steel, would not withstand such projectiles. There is no 300mm thick armor that is equivalent to 1200mm of steel, and therefore capable of stopping a projectile that will get stuck and stick out in the thickness of the armor plate. The success of protection against armor-piercing shells lies in the change in the vector of its impact on the surface of the armor. If you're lucky, then when you hit there will be only a small dent, and if you're not lucky, then the projectile will go through all the armor, regardless of whether it is thick or thin. Simply put, armor plates are relatively thin and hard, and the damaging effect depends largely on the nature of the interaction with the projectile. The American army uses depleted uranium to increase the hardness of armor, in other countries tungsten carbide, which is actually harder. About 80% of the ability of tank armor to stop blank projectiles falls on the first 10-20 mm of modern armor. Now consider the chemical effects of warheads. Chemical energy is represented by two types: HESH (Anti-tank armor-piercing high-explosive) and HEAT (HEAT projectile). HEAT - more common today, and has nothing to do with high temperatures. HEAT uses the principle of focusing the energy of an explosion into a very narrow jet. A jet is formed when a geometrically regular cone is surrounded by explosives from the outside. During detonation, 1/3 of the energy of the explosion is used to form a jet. It penetrates through the armor due to high pressure (not temperature). The simplest protection against this type of energy is a layer of armor set aside half a meter from the hull, which results in dissipation of the energy of the jet. This technique was used during the Second World War, when Russian soldiers lined the hull of the tank with a chain-link mesh from the beds. Now the Israelis are doing the same on the Merkava tank, they use steel balls hanging on chains to protect the stern from ATGMs and RPG grenades. For the same purposes, a large aft niche is installed on the tower, to which they are attached. Another method of protection is the use of dynamic or reactive armor. It is also possible to use combined dynamic and ceramic armor (such as Chobham). When a jet of molten metal comes into contact with reactive armor, the latter is detonated, the resulting shock wave defocuses the jet, eliminating its damaging effect. Chobham armor works in a similar way, but in this case, at the moment of the explosion, pieces of ceramic fly off, turning into a cloud of dense dust, which completely neutralizes the energy of the cumulative jet. HESH (High Explosive Anti-tank Armor Piercing) - the warhead works as follows: after the explosion, it flows around the armor like clay and transmits a huge momentum through the metal. Further, like billiard balls, the armor particles collide with each other and, thereby, the protective plates are destroyed. The booking material is capable of injuring the crew, scattering into small shrapnel. Protection against such armor is similar to that described above for HEAT. Summarizing the above, I would like to note that protection against the kinetic impact of a projectile comes down to a few centimeters of metallized armor, while protection against HEAT and HESH consists in creating a set aside armor, dynamic protection, as well as some materials (ceramics).

Reservation of modern domestic tanks

A. Tarasenko

Layered combined armor

In the 1950s, it became clear that a further increase in the protection of tanks was not possible only by improving the characteristics of armored steel alloys. This was especially true of protection against cumulative ammunition. The idea of using low-density fillers for protection against cumulative ammunition arose during the Great Patriotic War, the penetrating effect of a cumulative jet is relatively small in soils, this is especially true for sand. Therefore, it is possible to replace steel armor with a layer of sand sandwiched between two thin sheets of iron.

In 1957, VNII-100 carried out research to assess the anti-cumulative resistance of all domestic tanks, both serial production and prototypes. The protection of tanks was assessed based on the calculation of their shelling with a domestic non-rotating cumulative 85-mm projectile (in terms of its armor penetration it surpassed foreign cumulative shells of 90 mm caliber) at various heading angles provided for by the TTT in force at that time. The results of this research work formed the basis for the development of TTT to protect tanks from HEAT weapons. The calculations performed in the research showed that the experimental heavy tank "Object 279" and the medium tank "Object 907" had the most powerful armor protection.

Their protection ensured non-penetration by a cumulative 85-mm projectile with a steel funnel within the course angles: along the hull ± 60 ", the turret - + 90". To provide protection against a projectile of this type of other tanks, a thickening of the armor was required, which led to a significant increase in their combat weight: T-55 by 7700 kg, "Object 430" by 3680 kg, T-10 by 8300 kg and " Object 770" for 3500 kg.

An increase in the thickness of the armor to ensure the anti-cumulative resistance of the tanks and, accordingly, their mass by the above values was unacceptable. The specialists of the VNII-100 branch saw the solution to the problem of reducing the mass of armor in the use of fiberglass and light alloys based on aluminum and titanium, as well as their combination with steel armor, in the armor.

As part of combined armor, aluminum and titanium alloys were first used in the design of the armor protection of a tank turret, in which a specially provided internal cavity was filled with an aluminum alloy. For this purpose, a special aluminum casting alloy ABK11 was developed, which is not subjected to heat treatment after casting (due to the impossibility of providing a critical cooling rate during quenching of the aluminum alloy in a combined system with steel). The “steel + aluminum” option provided, with equal anti-cumulative resistance, a reduction in the mass of armor by half compared to conventional steel.

In 1959, the bow of the hull and the turret with two-layer armor protection "steel + aluminum alloy" were designed for the T-55 tank. However, in the process of testing such combined barriers, it turned out that the two-layer armor did not have sufficient survivability with repeated hits of armor-piercing-sub-caliber projectiles - the mutual support of the layers was lost. Therefore, further tests were carried out on three-layer armor barriers "steel+aluminum+steel", "titanium+aluminum+titanium". The gain in mass was somewhat reduced, but still remained quite significant: the combined “titanium + aluminum + titanium” armor compared to monolithic steel armor with the same level of armor protection when fired with 115-mm cumulative and sub-caliber projectiles provided a reduction weight by 40%, the combination of "steel + aluminum + steel" gave 33% weight savings.

T-64

In the technical project (April 1961) of the "432 product" tank, two filler options were initially considered:

· Steel armor casting with ultraforfor inserts with initial horizontal base thickness equal to 420 mm with equivalent anti-cumulative protection equal to 450 mm;

· a cast turret consisting of a steel armor base, an aluminum anti-cumulative jacket (poured after casting the steel hull) and outer steel armor and aluminum. The total maximum wall thickness of this tower is ~500 mm and is equivalent to ~460 mm anti-cumulative protection.

Both turret options resulted in over one ton of weight savings compared to an all-steel turret of equal strength. A turret with aluminum filler was installed on serial T-64 tanks.

Both turret options resulted in over one ton of weight savings compared to an all-steel turret of equal strength. A tower with aluminum filler was installed on serial tanks "product 432". In the course of accumulating experience, a number of shortcomings of the tower were revealed, primarily related to its large dimensions of the thickness of the frontal armor. Later, in the design of the armor protection of the tower on the T-64A tank in the period 1967-1970, steel inserts were used, after which they finally came to the originally considered version of the tower with ultraforfor inserts (balls), providing a given resistance with a smaller size. In 1961-1962 the main work on the creation of combined armor took place at the Zhdanovsky (Mariupol) metallurgical plant, where the technology of two-layer castings was debugged, various types of armor barriers were fired. Samples (“sectors”) were cast and tested with 85-mm cumulative and 100-mm armor-piercing projectiles

combined armor "steel+aluminum+steel". To eliminate the “squeezing out” of aluminum inserts from the body of the tower, it was necessary to use special jumpers that prevented the “squeezing out” of aluminum from the cavities of the steel tower. . Before the advent of the Object 432 tank, all armored vehicles had monolithic or composite armor.

A fragment of a drawing of a tank turret object 434 indicating the thicknesses of steel barriers and filler

Read more about the armor protection of the T-64 in the material -

The use of aluminum alloy ABK11 in the design of armor protection of the upper frontal part of the hull (A) and the front of the turret (B)

experienced medium tank "Object 432". The armored design provided protection against the effects of cumulative ammunition.

The upper frontal sheet of the hull "product 432" is installed at an angle of 68 ° to the vertical, combined, with a total thickness of 220 mm. It consists of an outer armor plate 80 mm thick and an inner fiberglass sheet 140 mm thick. As a result, the calculated resistance from cumulative ammunition was 450 mm. The front roof of the hull is made of armor 45 mm thick and had lapels - “cheekbones” located at an angle of 78 ° 30 to the vertical. The use of fiberglass of a selected thickness also provided reliable (in excess of TTT) anti-radiation protection. The absence in the technical design of the back plate after the fiberglass layer shows the complex search for the right technical solutions for creating the optimal three-barrier barrier, which developed later.

In the future, this design was abandoned in favor of a simpler design without "cheeks", which had greater resistance to cumulative ammunition. The use of combined armor on the T-64A tank for the upper frontal part (80 mm steel + 105 mm fiberglass + 20 mm steel) and a turret with steel inserts (1967-1970), and later with a filler of ceramic balls (horizontal thickness 450 mm) made it possible to provide protection against BPS (with armor penetration of 120 mm / 60 ° from a distance of 2 km) at a distance of 0.5 km and from COPs (penetrating 450 mm) with an increase in armor weight by 2 tons compared to the T-62 tank.

Scheme of the technological process of casting the tower "object 432" with cavities for aluminum filler. During shelling, the turret with combined armor provided full protection against 85-mm and 100-mm HEAT shells, 100-mm armor-piercing blunt-headed shells and 115-mm sub-capiber shells at firing angles of ±40 °, as well as protection against 115- mm of a cumulative projectile at a heading angle of fire of ±35 °.

High-strength concrete, glass, diabase, ceramics (porcelain, ultraporcelain, uralite) and various fiberglass were tested as fillers. Of the tested materials, inserts made of high-strength ultra-porcelain (the specific jet-extinguishing ability is 2–2.5 times higher than that of armored steel) and AG-4S fiberglass had the best characteristics. These materials were recommended for use as fillers in combined armor barriers. The weight gain when using combined armor barriers compared to monolithic steel barriers was 20-25%.

T-64A

In the process of improving the combined protection against the tower with the use of aluminum filler, they refused. Simultaneously with the development of the design of the tower with ultra-porcelain filler in the VNII-100 branch at the suggestion of V.V. Jerusalem, the design of the tower was developed using high-hard steel inserts intended for the manufacture of shells. These inserts, heat treated by differential isothermal hardening, had a particularly hard core and relatively less hard but more ductile outer surface layers. The manufactured experimental turret with high-hard inserts showed even better results in terms of durability during shelling than with filled ceramic balls.

The disadvantage of the tower with high-hard inserts was the insufficient survivability of the welded joint between the retaining plate and the tower support, which, when hit by an armor-piercing sub-caliber projectile, was destroyed without penetration.

In the process of manufacturing an experimental batch of turrets with high-hard inserts, it turned out to be impossible to provide the minimum required impact strength (high-hard inserts of the finished batch during shelling gave increased brittle fracture and penetration). Further work in this direction was abandoned.

(1967-1970)

In 1975, a corundum-filled turret developed by VNIITM was put into service (in production since 1970). Reservation of the tower - 115 steel cast armor, 140 mm ultra-porcelain balls and the rear wall of 135 mm steel with an angle of inclination of 30 degrees. casting technology towers with ceramic filling was worked out as a result of the joint work of VNII-100, Kharkov Plant No. 75, South Ural Radioceramics Plant, VPTI-12 and NIIBT. Using the experience of working on the combined armor of the hull of this tank in 1961-1964. The design bureaus of the LKZ and ChTZ factories, together with VNII-100 and its Moscow branch, developed variants of hulls with combined armor for tanks with guided missile weapons: "Object 287", "Object 288", "Object 772" and "Object 775".

corundum ball

Tower with corundum balls. The size of the frontal protection is 400 ... 475 mm. The stern of the tower is -70 mm.

Subsequently, the armor protection of Kharkov tanks was improved, including in the direction of using more advanced barrier materials, so from the end of the 70s on the T-64B, steels of the BTK-1Sh type were used, made by electroslag remelting. On average, the resistance of an equal-thickness sheet obtained by ESR is 10 ... 15 percent more than armored steels of increased hardness. In the course of mass production until 1987, the turret was also improved.

T-72 "Ural"

Booking VLD T-72 "Ural" was similar to booking T-64. In the first series of the tank, turrets directly converted from T-64 turrets were used. Subsequently, a monolithic tower made of cast armored steel was used, with a size of 400-410 mm. Monolithic towers provided satisfactory resistance against 100-105 mm armor-piercing sub-caliber projectiles(BTS) , but the anti-cumulative resistance of these towers in terms of protection against shells of the same caliber was inferior to towers with a combined filler.

Monolithic tower made of cast armor steel T-72,

also used on the export version of the T-72M tank

T-72A

The armor of the front part of the hull was reinforced. This was achieved by redistributing the thickness of the steel armor plates in order to increase the thickness of the back plate. Thus, the thickness of the VLD was 60 mm steel, 105 mm STB and the back sheet 50 mm thick. At the same time, the size of the reservation remained the same.

The turret armor has undergone major changes. In serial production, cores made of non-metallic molding materials were used as a filler, fastened before pouring with metal reinforcement (the so-called sand cores).

Tower T-72A with sand rods,

Also used on export versions of the T-72M1 tank

photo http://www.tank-net.com

In 1976, UVZ made attempts to produce turrets used on the T-64A with lined corundum balls, but it was not possible to master such technology there. This required new production facilities and the development of new technologies that had not been created. The reason for this was the desire to reduce the cost of the T-72A, which were also massively supplied to foreign countries. Thus, the resistance of the tower from the BPS of the T-64A tank exceeded the resistance of the T-72 by 10%, and the anti-cumulative resistance was 15 ... 20% higher.

Frontal part T-72A with redistribution of thicknesses

and increased protective back layer.

With an increase in the thickness of the back sheet, the three-layer barrier increases resistance.

This is a consequence of the fact that a deformed projectile acts on the rear armor, which partially collapsed in the first steel layer.

and lost not only speed, but also the original shape of the warhead.

The weight of three-layer armor required to achieve the level of resistance equivalent in weight to steel armor decreases with decreasing thickness.

front armor plate up to 100-130 mm (in the direction of fire) and a corresponding increase in the thickness of the rear armor.

The middle fiberglass layer has little effect on the projectile resistance of a three-layer barrier (I.I. Terekhin, Research Institute of Steel) .

Frontal part of PT-91M (similar to T-72A)

T-80B

Strengthening the protection of the T-80B was carried out through the use of rolled armor of increased hardness of the BTK-1 type for hull parts. The frontal part of the hull had an optimal ratio of three-barrier armor thicknesses similar to that proposed for the T-72A.

In 1969, a team of authors from three enterprises proposed a new bulletproof armor of the BTK-1 brand of increased hardness (dotp = 3.05-3.25 mm), containing 4.5% nickel and additives of copper, molybdenum and vanadium. . In the 70s, a complex of research and production work was carried out on BTK-1 steel, which made it possible to start introducing it into the production of tanks.

The results of testing stamped boards with a thickness of 80 mm from BTK-1 steel showed that they are equivalent in terms of resistance to serial boards with a thickness of 85 mm. This type of steel armor was used in the manufacture of the hulls of the T-80B and T-64A(B) tanks. The BTK-1 is also used in the design of the filler package in the turret of the T-80U (UD), T-72B tanks. The BTK-1 armor has increased projectile resistance against sub-caliber projectiles at firing angles of 68-70 (5-10% more compared to serial armor). As the thickness increases, the difference between the resistance of the BTK-1 armor and serial armor of medium hardness, as a rule, increases.

During the development of the tank, there were attempts to create a cast turret from steel with increased hardness, which were unsuccessful. As a result, the design of the turret was chosen from cast armor of medium hardness with a sand core, similar to the turret of the T-72A tank, and the thickness of the armor of the T-80B turret was increased, such turrets were accepted for serial production from 1977.

Further reinforcement of the armor of the T-80B tank was achieved in the T-80BV, which was put into service in 1985. The armor protection of the frontal part of the hull and turret of this tank is fundamentally the same as on the T-80B tank, but consists of reinforced combined armor and hinged dynamic protection "Contact-1". During the transition to serial production of the T-80U tank, some T-80BV tanks of the latest series (object 219RB) were equipped with towers of the T-80U type, but with the old FCS and the Cobra guided weapon system.

Tanks T-64, T-64A, T-72A and T-80B According to the criteria of production technology and the level of resistance, it can be conditionally attributed to the first generation of the implementation of combined armor on domestic tanks. This period has a framework within the mid-60s - early 80s. The armor of the tanks mentioned above generally provided high resistance to the most common anti-tank weapons (PTS) of the specified period. In particular, resistance to armor-piercing projectiles of the type (BPS) and feathered armor-piercing sub-caliber projectiles with a composite core of the type (OBPS). An example is the BPS L28A1, L52A1, L15A4 and OBPS M735 and BM22 types. Moreover, the development of the protection of domestic tanks was carried out precisely taking into account the provision of resistance against OBPS with an integral active part of the BM22.

But corrections to this situation were made by the data obtained as a result of the shelling of these tanks obtained as trophies during the Arab-Israeli war of 1982, the M111 type OBPS with a tungsten-based monoblock carbide core and a highly effective damping ballistic tip.

One of the conclusions of the special commission to determine the projectile resistance of domestic tanks was that the M111 has advantages over the domestic 125 mm BM22 projectile in terms of penetration at an angle of 68° combined armor VLD serial domestic tanks. This gives reason to believe that the M111 projectile was worked out mainly to destroy the VLD of the T72 tank, taking into account its design features, while the BM22 projectile was worked out on monolithic armor at an angle of 60 degrees.

In response to this, after the completion of the ROC "Reflection" for tanks of the above types, during the overhaul at the repair plants of the USSR Ministry of Defense, tanks since 1984 have been additionally strengthened by the upper frontal part. In particular, an additional plate with a thickness of 16 mm was installed on the T-72A, which provided an equivalent resistance of 405 mm from the M111 OBPS at a conditional damage limit speed of 1428 m / s.

The fighting in 1982 in the Middle East also had an impact on the anti-cumulative protection of tanks. From June 1982 to January 1983. During the implementation of the development work "Contact-1" under the leadership of D.A. Rototaeva (Scientific Research Institute of Steel) carried out work on the installation of dynamic protection (DZ) on domestic tanks. The impetus for this was the effectiveness of the Israeli Blazer-type remote sensing system demonstrated during the hostilities. It is worth recalling that DZ was developed in the USSR already in the 50s, but for a number of reasons it was not installed on tanks. These issues are discussed in more detail in the article.

Thus, since 1984, to improve the protection of tanksT-64A, T-72A and T-80B measures were taken as part of the ROC "Reflection" and "Contact-1", which ensured their protection from the most common PTS of foreign countries. In the course of mass production, the T-80BV and T-64BV tanks already took into account these solutions and were not equipped with additional welded plates.

The level of three-barrier (steel + fiberglass + steel) armor protection of the T-64A, T-72A and T-80B tanks was ensured by selecting the optimal thickness and hardness of the materials of the front and rear steel barriers. For example, an increase in the hardness of the steel front layer leads to a decrease in the anti-cumulative resistance of combined barriers installed at large structural angles (68 °). This is due to a decrease in the flow rate of the cumulative jet for penetration into the front layer and, consequently, an increase in its share involved in deepening the cavity.

But these measures were only modernization solutions, in tanks, the production of which began in 1985, such as the T-80U, T-72B and T-80UD, new solutions were applied, which can conditionally be attributed to the second generation of combined armor implementation . In the design of VLD, a design with an additional inner layer (or layers) between the non-metallic filler began to be used. Moreover, the inner layer was made of high-hardness steel.An increase in the hardness of the inner layer of steel combined barriers located at large angles leads to an increase in the anti-cumulative resistance of the barriers. For small angles, the hardness of the middle layer has no significant effect.

(steel+STB+steel+STB+steel).

On the new T-64BV tanks, additional armor for the VLD hull was not installed, since the new design was already

adapted to protect against new generation BPS - three layers of steel armor, between which two layers of fiberglass are placed, with a total thickness of 205 mm (60 + 35 + 30 + 35 + 45).

With a smaller overall thickness, the VLD of the new design in terms of resistance (excluding DZ) against BPS was superior to the VLD of the old design with an additional 30 mm sheet.

A similar VLD structure was also used on the T-80BV.

There were two directions in the creation of new combined barriers.

The first one developed in the Siberian Branch of the Academy of Sciences of the USSR (Institute of Hydrodynamics named after Lavrentiev, V. V. Rubtsov, I. I. Terekhin). This direction was a box-shaped (box-type plates filled with polyurethane foam) or cellular structure. The cellular barrier has increased anti-cumulative properties. Its principle of counteraction is that, due to the phenomena occurring at the interface between two media, part of the kinetic energy of the cumulative jet, which initially passed into the head shock wave, is transformed into the kinetic energy of the medium, which re-interacts with the cumulative jet.

The second proposed Research Institute of Steel (L.N. Anikina, M.I. Maresev, I.I. Terekhin). When a combined barrier (steel plate - filler - thin steel plate) is penetrated by a cumulative jet, a dome-shaped buckling of a thin plate occurs, the top of the bulge moves in the direction normal to the rear surface of the steel plate. This movement continues after breaking through the thin plate during the entire time the jet passes through the composite barrier. With optimally selected geometric parameters of these composite barriers, after they are pierced by the head part of the cumulative jet, additional collisions of its particles with the edge of the hole in the thin plate occur, leading to a decrease in the penetrating ability of the jet. Rubber, polyurethane, and ceramics were studied as fillers.

This type of armor is similar in principle to British armor. Burlington, which was used on Western tanks in the early 80s.

Further development of the design and manufacturing technology of cast towers consisted in the fact that the combined armor of the frontal and side parts of the tower was formed due to a cavity open from above, into which a complex filler was mounted, closed from above by welded covers (plugs). Turrets of this design are used on later modifications of the T-72 and T-80 tanks (T-72B, T-80U and T-80UD).

The T-72B used turrets with filler in the form of plane-parallel plates (reflective sheets) and inserts made of high-hardness steel.

On T-80U with a filler of cellular cast blocks (cellular casting), filled with polymer (polyether urethane), and steel inserts.

T-72B

Reservation of the turret of the T-72 tank is of the "semi-active" type.In front of the turret there are two cavities located at an angle of 54-55 degrees to the longitudinal axis of the gun. Each cavity contains a pack of 20 30mm blocks, each consisting of 3 layers glued together. Block layers: 21mm armor plate, 6mm rubber layer, 3mm metal plate. 3 thin metal plates are welded to the armor plate of each block, providing a distance between the blocks of 22 mm. Both cavities have a 45 mm armor plate located between the package and the inner wall of the cavity. The total weight of the contents of the two cavities is 781 kg.

The appearance of the T-72 tank reservation package with reflective sheets

And inserts of steel armor BTK-1

Package photo J. Warford. Journal of military ordnance. May 2002,

The principle of operation of bags with reflective sheets

The armor of the VLD of the T-72B hull of the first modifications consisted of composite armor made of steel of medium and increased hardness. The increase in resistance and the equivalent reduction in the armor-piercing effect of the ammunition is ensured by the flow rate at the media separation. A steel type-setting barrier is one of the simplest design solutions for an anti-ballistic protective device. Such a combined armor of several steel plates provided a 20% gain in mass compared to homogeneous armor, maybe with the same overall dimensions.

Later, a more complex booking option was used using "reflective sheets" on the principle of functioning similar to the package used in the tank turret.

DZ "Contact-1" was installed on the tower and hull of the T-72B. Moreover, the containers are installed directly on the tower without giving them an angle that ensures the most efficient operation of the remote sensing.As a result of this, the effectiveness of the remote sensing system installed on the tower was significantly reduced. A possible explanation is that during state tests of the T-72AV in 1983, the test tank was hit due to the presence of areas not covered by containers, the DZ and the designers tried to achieve a better overlap of the tower.

Starting from 1988, the VLD and the tower were reinforced with the DZ "Kontakt-V» providing protection not only from cumulative PTS, but also from OBPS.

The armor structure with reflective sheets is a barrier consisting of 3 layers: plate, gasket and thin plate.

Penetration of a cumulative jet into armor with "reflective" sheets

X-ray image showing lateral displacements of jet particles

And the nature of the deformation of the plate

The jet, penetrating the slab, creates stresses leading first to local swelling of the back surface (a) and then to its destruction (b). In this case, significant swelling of the gasket and the thin sheet occurs. When the jet pierces the gasket and the thin plate, the latter has already begun to move away from the rear surface of the plate (c). Since there is a certain angle between the direction of motion of the jet and the thin plate, at some point in time the plate begins to run into the jet, destroying it. The effect of the use of "reflective" sheets can reach 40% in comparison with monolithic armor of the same mass.

T-80U, T-80UD

When improving the armor protection of tanks 219M (A) and 476, 478, various options for obstacles were considered, the feature of which was the use of the energy of the cumulative jet itself to destroy it. These were box and cellular type fillers.

In the accepted version, it consists of cellular cast blocks, filled with polymer, with steel inserts. Hull armor is provided by optimal the ratio of the thicknesses of the fiberglass filler and steel plates of high hardness.

Tower T-80U (T-80UD) has an outer wall thickness of 85 ... 60 mm, the rear - up to 190 mm. In the cavities open at the top, a complex filler was mounted, which consisted of cellular cast blocks poured with polymer (PUM) installed in two rows and separated by a 20 mm steel plate. A BTK-1 plate with a thickness of 80 mm is installed behind the package.On the outer surface of the forehead of the tower within the heading angle + 35 installed solid V -shaped blocks of dynamic protection "Contact-5". On the early versions of the T-80UD and T-80U, the NKDZ "Contact-1" was installed.

For more information about the history of the creation of the T-80U tank, see the film -Video about the T-80U tank (object 219A)

Reservation of VLD is multi-barrier. Since the early 1980s, several design options have been tested.

How packages work "cellular filler"

This type of armor implements the method of so-called "semi-active" protection systems, in which the energy of the weapon itself is used for protection.

The method proposed by the Institute of Hydrodynamics of the Siberian Branch of the USSR Academy of Sciences and is as follows.

Scheme of action of cellular anti-cumulative protection:

1 - cumulative jet; 2- liquid; 3 - metal wall; 4 - shock wave of compression;

5 - secondary compression wave; 6 - collapse of the cavity

Scheme of single cells: a - cylindrical, b - spherical

Steel armor with polyurethane (polyetherurethane) filler

The results of studies of samples of cellular barriers in various design and technological versions were confirmed by full-scale tests during shelling with cumulative projectiles. The results showed that the use of a cellular layer instead of fiberglass can reduce the overall dimensions of the barrier by 15%, and the weight by 30%. Compared to monolithic steel, a layer weight reduction of up to 60% can be achieved while maintaining a close dimension to it.

The principle of operation of the armor of the "split" type.

In the back part of the cellular blocks there are also cavities filled with polymeric material. The principle of operation of this type of armor is approximately the same as that of cellular armor. Here, too, the energy of the cumulative jet is used for protection. When the cumulative jet, moving, reaches the free back surface of the barrier, the elements of the barrier near the free rear surface under the action of the shock wave begin to move in the direction of the jet. If, however, conditions are created under which the material of the obstacle moves onto the jet, then the energy of the elements of the obstacle flying from the free surface will be spent on the destruction of the jet itself. And such conditions can be created by making hemispherical or parabolic cavities on the rear surface of the barrier.

Some variants of the upper frontal part of the T-64A, T-80 tanks, the T-80UD (T-80U), T-84 variant and the development of a new modular VLD T-80U (KBTM)

T-64A tower filler with ceramic balls and T-80UD package options -

cellular casting (filler from cellular cast blocks filled with polymer)

and metal package

Further design improvements was associated with the transition to towers with a welded base. Developments aimed at increasing the dynamic strength characteristics of cast armor steels in order to increase the projectile resistance, gave a significantly smaller effect than similar developments for rolled armor. In particular, in the 80s, new steels of increased hardness were developed and ready for mass production: SK-2Sh, SK-3Sh. Thus, the use of towers with a rolled base made it possible to increase the protective equivalent along the base of the tower without increasing the mass. Such developments were undertaken by the Research Institute of Steel together with design bureaus, the tower with a rolled base for the T-72B tank had a slightly increased (by 180 liters) internal volume, the weight increase was up to 400 kg compared to the serial cast turret of the T-72B tank.

Var and turret ant of the improved T-72, T-80UD with a welded base

and ceramic-metal package, not used in series

The tower filler package was made using ceramic materials and steel of increased hardness or from a package based on steel plates with "reflective" sheets. Worked out options for towers with removable modular armor for the frontal and side parts.

T-90S/A

With regard to tank turrets, one of the significant reserves for strengthening their anti-projectile protection or reducing the mass of the steel base of the tower while maintaining the existing level of anti-projectile protection is to increase the resistance of steel armor used for turrets. The base of the T-90S / A tower is made made of steel armor of medium hardness, which significantly (by 10-15%) surpasses cast armor of medium hardness in terms of projectile resistance.

Thus, with the same mass, a tower made of rolled armor can have a higher anti-ballistic resistance than a tower made of cast armor, and, in addition, if rolled armor is used for a tower, its anti-ballistic resistance can be further increased.

An additional advantage of a rolled turret is the possibility of ensuring higher accuracy of its manufacture, since in the manufacture of a cast armor base of a turret, as a rule, the required casting quality and casting accuracy in terms of geometric dimensions and weight are not ensured, which necessitates labor-intensive and non-mechanized work to eliminate casting defects, adjustment of dimensions and weight of the casting, including adjustment of cavities for fillers. Realization of the advantages of the design of a rolled turret in comparison with a cast turret is possible only when its projectile resistance and survivability at the locations of the joints of parts made of rolled armor meets the general requirements for projectile resistance and survivability of the turret as a whole. Welded joints of the T-90S/A turret are made with full or partial overlapping of the joints of parts and welds from the side of shell fire.

The armor thickness of the side walls is 70 mm, the frontal armor walls are 65-150 mm thick; the turret roof is welded from separate parts, which reduces the rigidity of the structure during high-explosive impact.On the outer surface of the forehead of the tower are installed V -shaped blocks of dynamic protection.

Variants of towers with a welded base T-90A and T-80UD (with modular armor)

Other armor materials:

Materials used:

Domestic armored vehicles. XX century: Scientific publication: / Solyankin A.G., Zheltov I.G., Kudryashov K.N. /

Volume 3. Domestic armored vehicles. 1946-1965 - M .: LLC "Publishing House" Zeikhgauz "", 2010.

M.V. Pavlova and I.V. Pavlova "Domestic armored vehicles 1945-1965" - TiV No. 3 2009

Theory and design of the tank. - T. 10. Book. 2. Comprehensive protection / Ed. d.t.s., prof. P. P . Isakov. - M .: Mashinostroenie, 1990.

J. Warford. The first look at Soviet special armor. Journal of military ordnance. May 2002.

You can often hear how armor compared according to the thickness of steel plates 1000, 800mm. Or, for example, that a certain projectile can break through some "n"-number of mm armor. The fact is that now these calculations are not objective. Modern armor cannot be described as equivalent to any thickness of homogeneous steel.

There are currently two types of threats: kinetic energy projectile and chemical energy. By kinetic threat is meant armor-piercing projectile or, more simply, a blank with great kinetic energy. In this case, it is impossible to calculate the protective properties armor based on the thickness of the steel plate. So, shells With depleted uranium or tungsten carbide pass through steel like a knife through butter and the thickness of any modern armor, if it were homogeneous steel, it would not withstand the impact of such shells. There is no armor 300mm thick, which is equivalent to 1200mm steel, and therefore capable of stopping projectile, which will get stuck and stick out in the thickness armored sheet. Success protection from armor-piercing shells lies in changing the vector of its impact on the surface armor.

If you're lucky, then when you hit there will be only a small dent, and if you're not lucky, then projectile will sew all armor regardless of whether it is thick or thin. Simply put, armor plates are relatively thin and hard, and the damaging effect largely depends on the nature of the interaction with projectile. In the American army to increase hardness armor used depleted uranium, in other countries Wolfram carbide, which is actually more solid. About 80% of tank armor's ability to stop shells-blanks fall on the first 10-20 mm of modern armor.

Now consider chemical impact of warheads.
Chemical energy is represented by two types: HESH (anti-tank armor-piercing high-explosive) and HEAT ( HEAT projectile).

HEAT - more common today, and has nothing to do with high temperatures. HEAT uses the principle of focusing the energy of an explosion into a very narrow jet. A jet is formed when a geometrically regular cone is surrounded on the outside explosives. During detonation, 1/3 of the energy of the explosion is used to form a jet. Due to high pressure (not temperature), it penetrates through armor. The simplest protection against this type of energy is a layer set aside half a meter from the body. armor, thus dissipating the energy of the jet. This technique was used during the Second World War, when Russian soldiers surrounded the body tank netting from the beds. Israelis are doing the same now. tank Merkava, they are for protection ATGM feeds and RPG grenades use steel balls hanging from chains. For the same purposes, a large aft niche is installed on the tower, to which they are attached.

Other method protection is the use dynamic or reactive armor. It is also possible to use combined dynamic and ceramic armor(such as Chobham). When a jet of molten metal comes into contact with reactive armor the detonation of the latter occurs, the resulting shock wave defocuses the jet, eliminating its damaging effect. Chobham Armor works in a similar way, but in this case, at the moment of the explosion, pieces of ceramic fly off, turning into a cloud of dense dust, which completely neutralizes the energy of the cumulative jet.

HESH (anti-tank armor-piercing high-explosive) - the warhead works as follows: after the explosion, it flows around armor like clay and transmits a huge momentum through the metal. Further, like billiard balls, the particles armor collide with each other and thus the protective plates are destroyed. Material booking capable of flying into small shrapnel, injuring the crew. Protection from such armor similar to the one described above for HEAT.

Summarizing the above, I would like to note that protection from kinetic impact projectile reduced to a few centimeters of metallized armor, it depends protection from HEAT and HESH is to create a delayed armor, dynamic protection, as well as some materials (ceramics).

Common types of armor that are used in tanks:
1. Steel armor. It's cheap and easy to make. It can be a monolithic bar or soldered from several plates. armor. The elevated temperature treatment increases the elasticity of the steel and improves the reflectivity against kinetic attack. Classic tanks M48 and T55 used this armor type.

2. Perforated steel armor. This sophisticated steel armor in which perpendicular holes are drilled. Holes are drilled at the rate of no more than 0.5 of the expected diameter. projectile. It is clear that the weight is reduced. armor by 40-50%, but the efficiency also drops by 30%. It does armor more porous, which to some extent protects against HEAT and HESH. Advanced types of this armor include solid cylindrical fillers in the holes, made, for example, of ceramics. Moreover, perforated armor placed on the tank in such a way that projectile fell perpendicular to the course of the drilled cylinders. Contrary to popular belief, initially the Leopard-2 tanks did not use Chobham armor type(type of dynamic armor with ceramics), and perforated steel.

3. Ceramic layered (Chobham type). Represents a combined armor from alternating metal and ceramic layers. The type of ceramic used is usually a mystery, but usually it is alumina (aluminum salts and sapphire), boron carbide (the simplest hard ceramic), and similar materials. Sometimes synthetic fibers are used to hold metal and ceramic plates together. Lately in layered armor ceramic matrix connections are used. Ceramic layered armor protects very well from a cumulative jet (due to defocusing of a dense metal jet), but also resists kinetic effects well. The layering also makes it possible to effectively resist modern tandem projectiles. The only problem with ceramic plates is that they cannot be bent, so the layered armor built from squares.

Alloys are used in ceramic laminate to increase its density. . This is a common technology by today's standards. The main material used is tungsten alloy or, in the case of 0.75% titanium alloy with depleted uranium. The problem here is that depleted uranium is extremely poisonous when inhaled.

4. dynamic armor. This is a cheap and relatively easy way to defend against HEAT rounds. It is a high explosive, squeezed between two steel plates. When hit by a warhead, explosives detonate. The disadvantage is the uselessness in the event of a kinetic impact projectile, as well as tandem projectile. However, such armor is lightweight, modular and simple. It can be seen, in particular, on Soviet and Chinese tanks. dynamic armor usually used instead advanced layered ceramic armor.

5. Abandoned armor. One of the tricks of design thought. In this case, at a certain distance from the main armor set aside light barriers. Effective only against a cumulative jet.

6. Modern combined armor. Most of the best tanks equipped with this armor type. In fact, a combination of the above types is used here.
———————
Translation from English.
Address: www.network54.com/Forum/211833/thread/1123984275/last-1124092332/Modern+Tank+Armor

Reservation of modern domestic tanks

A. Tarasenko

Layered combined armor

T-64

In the technical project (April 1961) of the "432 product" tank, two filler options were initially considered:

· Steel armor casting with ultraforfor inserts with initial horizontal base thickness equal to 420 mm with equivalent anti-cumulative protection equal to 450 mm;

Both turret options resulted in over one ton of weight savings compared to an all-steel turret of equal strength. A turret with aluminum filler was installed on serial T-64 tanks.

A fragment of a drawing of a tank turret object 434 indicating the thicknesses of steel barriers and filler

Read more about the armor protection of the T-64 in the material - Security of the tanks of the second post-war generation T-64 (T-64A), Chieftain Mk5R and M60

The use of aluminum alloy ABK11 in the design of armor protection of the upper frontal part of the hull (A) and the front of the turret (B)

experienced medium tank "Object 432". The armored design provided protection against the effects of cumulative ammunition.

T-64A

(1967-1970)

corundum ball

Tower with corundum balls. The size of the frontal protection is 400 ... 475 mm. The stern of the tower is -70 mm.

T-72 "Ural"

Monolithic tower made of cast armor steel T-72,

also used on the export version of the T-72M tank

T-72A

Tower T-72A with sand rods,

Also used on export versions of the T-72M1 tank

photo http://www.tank-net.com

Frontal part T-72A with redistribution of thicknesses

and increased protective back layer.

With an increase in the thickness of the back sheet, the three-layer barrier increases resistance.

This is a consequence of the fact that a deformed projectile acts on the rear armor, which partially collapsed in the first steel layer.

and lost not only speed, but also the original shape of the warhead.

The weight of three-layer armor required to achieve the level of resistance equivalent in weight to steel armor decreases with decreasing thickness.

front armor plate up to 100-130 mm (in the direction of fire) and a corresponding increase in the thickness of the rear armor.

The middle fiberglass layer has little effect on the projectile resistance of a three-layer barrier (I.I. Terekhin, Research Institute of Steel) .

Frontal part of PT-91M (similar to T-72A)

T-80B

(steel+STB+steel+STB+steel).

On the new T-64BV tanks, additional armor for the VLD hull was not installed, since the new design was already

adapted to protect against new generation BPS - three layers of steel armor, between which two layers of fiberglass are placed, with a total thickness of 205 mm (60 + 35 + 30 + 35 + 45).

With a smaller overall thickness, the VLD of the new design in terms of resistance (excluding DZ) against BPS was superior to the VLD of the old design with an additional 30 mm sheet.

A similar VLD structure was also used on the T-80BV.

There were two directions in the creation of new combined barriers.

This type of armor is similar in principle to British armor. Burlington, which was used on Western tanks in the early 80s.

The T-72B used turrets with filler in the form of plane-parallel plates (reflective sheets) and inserts made of high-hardness steel.

On T-80U with a filler of cellular cast blocks (cellular casting), filled with polymer (polyether urethane), and steel inserts.

T-72B

The appearance of the T-72 tank reservation package with reflective sheets

And inserts of steel armor BTK-1

Package photo J. Warford. Journal of military ordnance. May 2002,

The principle of operation of bags with reflective sheets

Later, a more complex booking option was used using "reflective sheets" on the principle of functioning similar to the package used in the tank turret.

Starting from 1988, the VLD and the tower were reinforced with the DZ "Kontakt-V» providing protection not only from cumulative PTS, but also from OBPS.

The armor structure with reflective sheets is a barrier consisting of 3 layers: plate, gasket and thin plate.

Penetration of a cumulative jet into armor with "reflective" sheets

X-ray image showing lateral displacements of jet particles

And the nature of the deformation of the plate

T-80U, T-80UD

For more information about the history of the creation of the T-80U tank, see the film -Video about the T-80U tank (object 219A)

Reservation of VLD is multi-barrier. Since the early 1980s, several design options have been tested.

How packages work "cellular filler"

This type of armor implements the method of so-called "semi-active" protection systems, in which the energy of the weapon itself is used for protection.

The method proposed by the Institute of Hydrodynamics of the Siberian Branch of the USSR Academy of Sciences and is as follows.

Scheme of action of cellular anti-cumulative protection:

1 - cumulative jet; 2- liquid; 3 - metal wall; 4 - shock wave of compression;

5 - secondary compression wave; 6 - collapse of the cavity

Scheme of single cells: a - cylindrical, b - spherical

Steel armor with polyurethane (polyetherurethane) filler

The principle of operation of the armor of the "split" type.

Some variants of the upper frontal part of the T-64A, T-80 tanks, the T-80UD (T-80U), T-84 variant and the development of a new modular VLD T-80U (KBTM)

T-64A tower filler with ceramic balls and T-80UD package options -

cellular casting (filler from cellular cast blocks filled with polymer)

and metal package

Var and turret ant of the improved T-72, T-80UD with a welded base

and ceramic-metal package, not used in series

T-90S/A

Variants of towers with a welded base T-90A and T-80UD (with modular armor)

Other armor materials:

Materials used:

Domestic armored vehicles. XX century: Scientific publication: / Solyankin A.G., Zheltov I.G., Kudryashov K.N. /

Volume 3. Domestic armored vehicles. 1946-1965 - M .: LLC "Publishing House" Zeikhgauz "", 2010.

M.V. Pavlova and I.V. Pavlova "Domestic armored vehicles 1945-1965" - TiV No. 3 2009

Theory and design of the tank. - T. 10. Book. 2. Comprehensive protection / Ed. d.t.s., prof. P. P . Isakov. - M .: Mashinostroenie, 1990.

J. Warford. The first look at Soviet special armor. Journal of military ordnance. May 2002.

Combined armor, also composite armor, less commonly multi-layer armor is a type of armor consisting of two or more layers of metallic or non-metallic materials. "A passive defense system (design) containing at least two different materials (not counting air gaps) designed to provide balanced protection against HEAT and kinetic munitions used in the ammunition load of a single high-pressure gun."
In the post-war period, the main means of defeating heavy armored targets (main battle tank, MBT) were cumulative weapons, represented primarily by anti-tank guided missiles (ATGMs) that were dynamically developing in the 1950s and 1960s, the armor-piercing ability of combat units of which by the beginning 1960s exceeded 400 mm of armor steel.
The answer to parry the threat from cumulative weapons was found in the creation of multi-layer combined armor with a higher, compared to homogeneous steel armor, anti-cumulative resistance, containing materials and design solutions that together provide an increased jet-extinguishing ability of armor protection. Later, in the 1970s, armor-piercing feathered sabots of 105 and 120 mm tank guns with a heavy alloy core were adopted and widely used in the West, providing protection against which turned out to be a much more difficult task.
The development of combined armor for tanks was started almost simultaneously in the USSR and the USA in the second half of the 1950s and was used on a number of experimental US tanks of that period. However, among production tanks, combined armor was used on the Soviet T-64 main battle tank, whose production began in 1964, and was used on all subsequent main battle tanks of the USSR.
On serial tanks of other countries, combined armor of various schemes appeared in 1979-1980 on the Leopard 2 and Abrams tanks and since the 1980s has become the standard in world tank building. In the United States, combined armor for the armored hull and turret of the Abrams tank, under the general designation "Special Armor", reflecting the secrecy of the project, or "Burlington", was developed by the Ballistic Research Laboratory (BRL) by 1977, included ceramic elements, and was designed to protect against cumulative ammunition (equivalent thickness for steel no worse than 600 ... 700 mm), and armor-piercing finned shells of the BOPS type (equivalent thickness for steel no worse than 350 ... mass in comparison with equally resistant steel armor, and on later serial modifications it was consistently increased. Due to the high cost compared to homogeneous armor and the need to use armor barriers of great thickness and mass to protect against modern cumulative ammunition, the use of combined armor is limited to main battle tanks and, less often, main or mounted additional armor for infantry fighting vehicles and other light category armored vehicles.

Related concepts

A cumulative-fragmentation projectile (KOS, sometimes also called a multifunctional projectile) is a main-purpose artillery ammunition that combines a pronounced cumulative and weaker high-explosive fragmentation action.

Armored shield - a protective device mounted on a weapon (for example, a machine gun or a gun). Used to protect the gun crew from bullets and shrapnel. Also called an armor shield is a device made from improvised materials, sometimes used in the field to protect the shooter from fire.

Multi-barreled layout - a type of armored vehicle layout scheme, in which the main armament of an armored vehicle unit includes more than one cannon, gun or mortar, or one or more multi-barreled artillery systems (not counting additional barreled weapons, such as machine guns of various types or externally mounted recoilless rifles). Due to a number of reasons of a technical and technological nature, a multi-barrel layout is used mainly in the creation of self-propelled ...

Armored (protective) window - a translucent structure that protects people and material assets in the room from damage or penetration from the outside through the window opening.

Gusmatik, or gusmatic tire - a wheel tire filled with an elastic mass. Widely used in military equipment in the first half of the 20th century, now gummatics are practically out of use and are used to a limited extent only on some special (construction, etc.) machines.

Ship armor is a protective layer that has a sufficiently high strength and is designed to protect parts of the ship from the effects of enemy weapons.

Krupp cemented armor (K.C.A.) is a variant of the further development of Krupp armor. The fabrication process is largely the same with slight changes in the composition of the alloy: 0.35% carbon, 3.9% nickel, 2.0% chromium, 0.35% manganese, 0.07% silicon, 0.025% phosphorus, 0.020% sulfur . K.C.A. had the hard surface of the Krupp armor through the use of carbonaceous gases, but also had a higher "fiber" elasticity in the back of the sheet. This increased elasticity...

Bottom gas generator - a device at the rear of some artillery shells that increases their range by up to 30%.

Object 172-2M "Buffalo" - Soviet experienced main battle tank. Created in the design bureau of Uralvagonzavod. Not serially produced.

The relic is a third-generation Russian modular dynamic protection complex developed by the Research Institute of Steel, which was put into service in 2006 to unify the T-72B2 Ural, T-90SM and T-80 tanks in terms of protection level. It is an evolutionary development of the Soviet complex of dynamic protection "Contact-5"; designed to modernize armored vehicles of medium and heavy weight categories (BMPT combat vehicle, T-80BV, T-72B, T-90 tanks) to provide protection against most modern Western-made OBPS...

Active protection is a type of combat vehicle (BM) protection used in active mode on aircraft (LA), armored vehicles, and so on.

Tank (English tank) - an armored fighting vehicle, most often on a caterpillar track, usually with cannon armament, usually in a rotating full-rotation turret, designed mainly for direct fire. and after the Second World War, experiments were carried out to create tanks with rocket weapons as the main one. Variants of tanks with flamethrower weapons are known. Definitions...

Pneumatic weapon - a type of small arms in which the projectile takes off under the influence of a gas under pressure.

An armor-piercing aerial bomb (in the USSR Air Force and the USSR Navy Air Force was abbreviated BrAB or BRAB) is a class of aerial bombs designed to destroy objects with powerful armor protection (large warships, armored coastal batteries, armored structures of long-term defensive structures (armored domes, etc.). They could also hit all those targets (except for hard-surface runways), for the destruction of which concrete-piercing aerial bombs were regularly used....

Air bomb or air bomb, one of the main types of aviation weapons (ASP). It is dropped from an airplane or other aircraft, separating from the holders under the action of gravity or with a low initial speed (with forced separation).

A high-explosive fragmentation projectile (OFS) is a main-purpose artillery ammunition that combines fragmentation and high-explosive action and is designed to hit a large number of types of targets: defeating enemy manpower in open areas or in fortifications, destroying lightly armored vehicles, destroying buildings, fortifications and fortifications, making passages in minefields, etc.

Tochka (GRAU index - 9K79, under the INF Treaty - OTR-21) - Soviet tactical missile system of the divisional level (since the late 1980s transferred to the army level) developed by the Kolomna Design Bureau of Mechanical Engineering under the leadership of Sergei Pavlovich Invincible.

An anti-tank guided missile (abbr. ATGM) is a type of guided missile munitions designed to fire from barreled artillery and tank weapons (guns or guns). Often identified with an anti-tank guided missile (ATGM), although the two terms are not synonymous.

Small-caliber high-explosive projectile - a type of ammunition filled with explosives, the damaging effect of which is achieved mainly due to the shock wave formed during the explosion. This is its fundamental difference from fragmentation ammunition, whose damaging effect on the target is associated mainly with the fragmentation field formed as a result of fragmentation of the projectile body during the detonation of an explosive charge.

Sub-caliber ammunition - ammunition, the diameter of the warhead (core) of which is less than the diameter of the barrel. Most often used to combat armored targets. The increase in armor penetration compared to conventional armor-piercing ammunition occurs due to an increase in the initial velocity of ammunition and specific pressure in the process of penetrating armor. For the manufacture of the core, materials with the highest specific gravity are used - based on tungsten, depleted uranium and others. To stabilize...

"Tiger" - Russian multi-purpose off-road vehicle, armored car, army off-road vehicle. Produced at the Arzamas Machine-Building Plant with YaMZ-5347-10 (Russia), Cummins B-205 engines. Some early models were equipped with GAZ-562 (licensed Steyr), Cummins B-180 and B-215 engines.

An anti-tank grenade is an explosive or incendiary device used by infantry to fight armored vehicles using muscle power or non-artillery devices. Anti-tank mines do not formally belong to this category of weapons, however, there were universal grenade mines and anti-aircraft mines similar in design to grenades. Anti-tank missiles may be classified as "grenades", depending on the national classification of such weapons ...

Mortar-mortar (English gun-mortar) - an artillery gun of an intermediate type between a mortar and a type of artillery system, which is currently called a mortar - having a short barrel (with a barrel length less than 15 calibers), loaded from the muzzle or from the breech barrel and mounted on a massive plate (moreover, the recoil momentum is transmitted to the plate not directly from the barrel, but indirectly through the design of the gun carriage). This design type has become widespread during ...

Cumulative effect, Munroe effect - strengthening the effect of an explosion by concentrating it in a given direction, achieved by using a charge with a notch opposite the location of the detonator and facing the target. The cumulative recess is usually conical in shape, covered with a metal lining, the thickness of which can vary from fractions of a millimeter to several millimeters.

Armor-piercing bullet - a special type of bullet designed to hit lightly armored targets. Refers to the so-called special ammunition, created to expand the tactical capabilities of small arms.